This article describes some simple ways of etching printed circuit boards, in case when no ferric chloride.
- Etching in solution of sulfuric acid and hydrogen peroxide.
The water cautiously pour in bathroom suicide sulphuric acid based 20-30 ml per cup of water. Then there is added 5-6 tablets of hydrogen peroxide. Size shivajut-subject to dissolution of tablets.
Etching fee in this solution takes place during 1-2 hours.
Treating acid needs to be especially careful.
Way to not be so dangerous and where whiter available if instead of evaporated milk include acid take electrolyte for car batteries. Electric lit need to dilute with water twice and finish 5-6 tablets of hydrogen peroxide for a glass of water.
- Etching in solution of nitric acid.
Nitric acid is required.
Раствор должен быть концентрацией не более 20%. Травление происходит быстро, – обычно не более 15 минут. После травления, чтобы нейтрализовать кислоту плату промывают раствором питьевой соды.
Данный способ является одним из наиболее опасных для здоровья. Кроме того, что кислотой можно обжечься, так еще и при травлении выделяется ядовитый газ – окись азота. Поэтому, такой способ травления вряд ли можно признать пригодным для использования в условиях квартиры или другого жилого помещения.
- Etching in solution mixture of POWA agreed salt and copper sulphate.
Этот способ наиболее безопасный в бытовых условиях. Но все же нужно понимать, что медный купорос – это тоже вещество, которым можно отравиться.
Раствор нужно готовить именно в такой последовательности: наливаете в ванночку воду. Затем, насыпаете поваренную соль из расчета – две столовых ложки на стакан воды, размешиваете её пластмассовой или стеклянной палочкой до растворения, и добавляете медный купорос из расчета – одна столовая ложка на стакан воды. Размешиваете неметаллическим предметом, и погружаете в раствор плату. Последовательность должна быть именно такая, – сначала растворить соль, потом медный купорос.
Etching occurs in salt, and copper sulfate acts as a catalyst.
Etching in this solution is very slow, and may reach 10 Cha. You can speed up the process of with the lid lifted up with a solution to a temperature of 60-70° c, for example, using electric lamps. In addition, very nice to somehow activate the mixing liquid. You can tray strengthening on, say, a piece of plywood and plywood put on soft rubber feet. Then on plywood near the bath attach BOR-machine, in which instead of drills, insert the bent bolt or nail. And enable. Vibration from boron-machines with such eccentric will be quite active rock bath and accelerate the etching process several times.
Заранее приготавливать сухую смесь медного купороса и поваренной соли не допускается, – сначала нужно растворить один компонент, а потом другой.
And yet, the best is etched in ferric chloride solution. If you cannot purchase this "reagent", it is possible to prepare itself independently.
10% glass-hydrochloric acid readily vsy 10-15 grams of small iron IRS Lok. Solution can withstand a few days before the brown coloring. After that you can slack off fee.
Etching in all cases must be carried out in non-metallic container, such as in the photo tray. At the same time, the fee must be rotated with stravlivaemoj foil side down, and is at a distance of not less than 5 mm to the bottom of the bath.
Author: Snegirev I.